7075 AEROSPACE ALUMINUM BAR

7075 is an aerospace aluminum bar with cold finished or extruded aluminum wrought alloy with high strength, adequate machinability and improved stress corrosion control. Fine grain control results in good tool wear.

7075 is one of the highest strength aluminum alloys. It has good fatigue strength and average machinability. Often used where parts are highly stressed. It is not weld able and has less corrosion resistance than other aluminum alloys. The mechanical properties depend on the temper of the material. Commonly used in the bicycle industry, aircraft structures.

When forging this metal, it is recommended that the temperature be set between 700 and 900 degrees. This should then be followed by solution heat treatment. It’s not recommended for welding to be used as a joining technique, but if needed, resistance welding can be used. It’s not recommended for arc welding to be used because it can lower the metal’s corrosion resistance.

Chemical Composition WT(%)
Silicon	Iron	Copper	Magnesium	Manganese	Chromium	Zinc	Titanium	Others	Aluminum
0.40	0.50	1.20~2.0	2.10~2.90	0.30	0.18~0.28	5.10~6.10	0.20	0.15	Balance

Typical Mechanical Properties
Temper	Diameter (mm)	Tensile Strength (Mpa)	Yield Strength (Mpa)	Elongation (%)	Hardnedd (HB)
T6,T651,T6511	≤25.00	≥540	≥480	≥7	150
	＞25.00~100.00	560	500	7	150
	＞100.00~150.00	550	440	5	150
	＞150.00~200.00	440	400	5	150
T73,T7351,T73511	≤25.00	485	420	7	135
	＞25.00~75.00	475	405	7	135
	＞75.00~100.00	470	390	6	135
	＞100.00~150.00	440	360	6	135