7075 AEROSPACE ALUMINUM BAR
7075 is an aerospace aluminum bar with cold finished or extruded aluminum wrought alloy with high strength, adequate machinability and improved stress corrosion control. Fine grain control results in good tool wear.
7075 is one of the highest strength aluminum alloys. It has good fatigue strength and average machinability. Often used where parts are highly stressed. It is not weld able and has less corrosion resistance than other aluminum alloys. The mechanical properties depend on the temper of the material. Commonly used in the bicycle industry, aircraft structures.
When forging this metal, it is recommended that the temperature be set between 700 and 900 degrees. This should then be followed by solution heat treatment. It’s not recommended for welding to be used as a joining technique, but if needed, resistance welding can be used. It’s not recommended for arc welding to be used because it can lower the metal’s corrosion resistance.
Chemical Composition WT(%) |
|||||||||
Silicon |
Iron |
Copper |
Magnesium |
Manganese |
Chromium |
Zinc |
Titanium |
Others |
Aluminum |
0.40 |
0.50 |
1.20~2.0 |
2.10~2.90 |
0.30 |
0.18~0.28 |
5.10~6.10 |
0.20 |
0.15 |
Balance |
Typical Mechanical Properties |
|||||
Temper |
Diameter (mm) |
Tensile Strength (Mpa) |
Yield Strength (Mpa) |
Elongation (%) |
Hardnedd (HB) |
T6,T651,T6511 | ≤25.00 |
≥540 |
≥480 |
≥7 |
150 |
>25.00~100.00 |
560 |
500 |
7 |
150 | |
>100.00~150.00 |
550 |
440 |
5 |
150 | |
>150.00~200.00 |
440 |
400 |
5 |
150 | |
T73,T7351,T73511 | ≤25.00 |
485 |
420 |
7 |
135 |
>25.00~75.00 |
475 |
405 |
7 |
135 | |
>75.00~100.00 |
470 |
390 |
6 |
135 | |
>100.00~150.00 |
440 |
360 |
6 |
135 |
Our Advantage
Inventory and Delivery
We have enough product in stock, we can offer enough material to customers. The lead time can be within 7 days for stock materil.
Quality
All the product are from the biggest manufacturer, we can offer the MTC to you. And we can also offer Third-Party test report.
Custom
We have cutting machine, custom size are available.