Factory best selling Aluminum 2014 - 1060 Aluminum Sheet Chemical Equipment Application 1060 H14 Aluminum – Miandi

Product Detail

Aluminium / Aluminum 1060 alloy is a low strength and pure Aluminium / Aluminum alloy with good corrosion resistance characteristic.

Aluminium / Aluminum 1060 alloy can be hardened only from cold working. Tempers H18, H16, H14 and H12 are determined based on the amount of cold working imparted to this alloy.

Aluminium / Aluminum 1060 alloy is rated with fair to poor machinability, especially in the soft temper conditions. The machinability is much improved in the harder (cold worked) tempers. Usage of lubricants and either high-speed steel tooling or carbide are recommended for this alloy. Some of the cutting for this alloy can also be done dry.

Aluminium / Aluminum 1060 alloy is widely used in the manufacture of railroad tank cars and chemical equipment.

Chemical Composition WT(%)
Silicon	Iron	Copper	Magnesium	Manganese	Chromium	Zinc	Titanium	Others	Aluminum
0.25	0.35	0.05	0.03	0.03	-	0.05	0.03	0.03	99.6

Typical Mechanical Properties
Temper	Thickness (mm)	Tensile Strength (Mpa)	Yield Strength (Mpa)	Elongation (%)
H112	＞4.5~6.00	≥75	-	≥10
	＞6.00~12.50	≥75		≥10
	＞12.50~40.00	≥70		≥18
	＞40.00~80.00	≥60		≥22
H14	＞0.20~0.30	95~135	≥70	≥1
	＞0.30~0.50			≥2
	＞0.50~0.80			≥2
	＞0.80~1.50			≥4
	＞1.50~3.00			≥6
	＞3.00~6.00			≥10