5A06 Aluminum Alloy Plate For Boat Building

Product Detail

5A06 Aluminum Alloy

It is a high magnesium alloy with good strength, corrosion resistance, and machinability in non heat treatable alloys. The surface is aesthetically pleasing after anodizing treatment. The arc welding performance is good. The main alloying element in 5A06 alloy is magnesium, which has good corrosion resistance, weldability, and moderate strength. The excellent corrosion resistance of 5A06 alloy makes it widely used in maritime applications such as ships, as well as welding parts for automobiles, airplanes, subways, light rails, pressure vessels that require strict fire prevention (such as liquid tankers, refrigerated trucks, refrigerated containers), refrigeration devices, TV towers, drilling equipment, transportation equipment, missile parts, armor, etc

5A06 belongs to the Al Mg alloy series and has a wide range of applications, especially in the construction industry where it is indispensable. It is the most promising alloy. Good corrosion resistance, excellent weldability, good cold workability, and moderate strength. The main alloying element of 5083 is magnesium, which has good formability, corrosion resistance, weldability, and moderate strength. It is used to manufacture aircraft fuel tanks, oil pipes, as well as sheet metal parts for transportation vehicles and ships, instruments, street lamp brackets and rivets, hardware products, electrical enclosures, etc.

AL Mn alloy is the most widely used rust proof aluminum, which has high strength, especially fatigue resistance: high plasticity and corrosion resistance, cannot be strengthened by heat treatment, good plasticity during semi cold work hardening, low plasticity during cold work hardening, good corrosion resistance, good weldability, poor machinability, and can be polished. Mainly used for low load parts that require high plasticity and good weldability, working in liquid or gas media, such as oil tanks, gasoline or lubricant conduits, various liquid containers, and other low load parts made by deep drawing: wire is used to make rivets

Chemical Composition WT(%)
Silicon	Iron	Copper	Magnesium	Manganese	Chromium	Zinc	Titanium	Others	Aluminum
0.40	0.40	0.10	0.50~0.8	5.8~6.8	-	0.20	0.02~0.10	0.10	Remainder

Typical Mechanical Properties
Temper	Thickness (mm)	Tensile Strength (Mpa)	Yield Strength (Mpa)	Elongation (%)
O	0.50~4.5	≥315	≥155	≥16
H112	＞4.50~10.00	≥315	≥155	≥16
	＞10.00~12.50	≥305	≥145	≥12
	＞12.50~25.00	≥305	≥145	≥12
	＞25.00~50.00	≥295	≥135	≥6
F	＞4.50~150.00	-	-	-